Due to its low density, good mechanical properties and chemical inertness, glassy carbon(GC) has been studied for appications in several fields. A raw thermosetting resin of furanic resin was polymerized with a curing agent of p-toluenesulfonic acid monohydrate. The maximum yield of GC was obtained at the curing agent content of 1.0 wt% in furanic resin. In order to make thick GC, the affect of graphite filler addition to the furanic resin was investigated. The density and electrical resitivity of GC after graphitization were 1.45 g/cm3 and 47 ×10-4 Ω · cm respectively and the amorphous structure of GC was confirmed by XRD profiles with very broad peaks comparable to those of graphite at 206˚ and 45˚.