논문 상세보기
pp.264-271
PU type flame-retardant coatings (TBAO/L-75, TBAOL ; TBAO/N-100, TBAON) were prepared by blending bromine-containing modified polyester (TBAO) which was synthesized in our earlier work. with two kinds of isocyanate curing agents, Desmodur L-75 and Desmodur N-100. Physical properties of the prepared flame-retardant coatings were tested. TBAOL shows better hardness than TBAON, while TBAON shows better viscosity, accelerated weathering resistance, yellowness index and lightness index difference than TBAOL. There were no remarkable differences in fineness of grind, 60˚ specular gloss, cross-hatch adhesion, and abrasion resistance of TBAOL and TBAON. There was no discernable difference in flame-retardancy between the two flame-retardant coatings, TBAOL and TBAON. When the content of tribromo acetic acid, which is flame-retarding component, was 30wt% the LOI value was in a range of 29~30%, which indicates that the two coatings are good flame-retardant coatings.