Adsorption isotherms of p-nitrophenol from its aqueous solutions on two samples of activated carbon fibres and two samples of granulated activated carbons have been determined in the concentration range 40~800 mg/L (ppm). The surface of these carbons was modified by oxidation with nitric acid and oxygen gas, and by degassing the carbon surface under vacuum at temperatures of 400℃, 650℃ and 950℃. The oxidation of carbon enhances the amount of carbon-oxygen surface groups, while degassing decreases the amount of these surface groups. The adsorption of p-nitrophenol does not depend upon the surface area alone but appears to be influenced by the presence of oxygen groups on the carbon surface. The adsorption decreases on oxidation while the degassing of the carbon surface enhances the adsorption. The decrease in adsorption depends upon the strength of the oxidative treatment being much larger in case of the oxidation with nitric acid, while the decrease in adsorption on degassing depends upon the temperature of degassing. The results show that while the presence of acidic surface groups which are evolved as CO2 on degassing suppress the adsorption of p-nitrophenol, the presence of non acidic surface groups which are evolved as CO on degassing tend to enhance the adsorption. Suitable mechanisms compatible with the results have been presented.

• Meenakshi Goyal(Department of Chemical Engineering & Technology
  Panjab University)