In this study, TiO2-Activated carbon (AC) complex fibers were prepared by electrospinning for the synergetic effect of adsorption and degradation of organic pollutant. The average diameter of these fibers increased with increasing the amount of AC added, except for 1AC-TOF (AC/TiO2 =1/40 mass ratio). After calcinations at 500℃, long as-spun fibers were broken and their average diameter was slightly decreased. The resultant fibers after calcination had rough surface and sphere shapes like a peanut. From XRD results, it was confirmed that as-spun fibers were changed to anatase TiO2 fiber after calcinations at 500℃. The prepared TiO2-AC complex fibers could remove procian blue dyes by solar light irradiation with high removal property of 94~99%. The PB dye was rapidly removed by adsorption during the initial 5 minutes. But after 5 minutes, dye removal was occurred by photodegradation. In this study, the most efficient AC/TiO2 ratio of TiO2-AC complex fibers was 5/40, showing the synergetic effect of adsorption and photodegradation. It is expected that the TiO2-AC complex fibers can be used to remove of organic pollutants in water system.

• Min-Jung Jung(Department of Applied Chemistry and Biological Engineering, Chungnam National University)
• Eui-Gyung Jeong(Department of Applied Chemistry and Biological Engineering, Chungnam National University)
• Jeen-Seok Jang(Chungbuk Regional Small & Medium Business Administration)
• Young-Seak Lee(Department of Applied Chemistry and Biological Engineering, Chungnam National University)