Polyacetylene (PA) films with vertically aligned fibril morphology were synthesized in homeotropic nematic liquid crystal (N-LC) solvent by using a magnetic field of 5 Tesla as an external perturbation. Scanning electron microscope (SEM) photographs indicated that the lengths of fibrils from the substrate were 5-35μm, depending on polymerization time. Carbonization was carried out using iodine-doped PA film and a morphology-retaining carbonization method. From the SEM results, we confirmed that the vertical morphology of the PA remains unchanged even after carbonization at 800℃. The weight loss of the films due to carbonization at 800℃ is about 20% of the weight of the film before iodine doping. It is expected that vertically aligned carbon might be a precursor for preparing vertical graphite materials, which materials could be useful for electrochemical energy storage and cell electrodes.

• Munju Goh(Carbon Convergence Materials Research Center, Institute of Advanced Composite Materials, Korea Institute of Science and Technology (KIST)) Corresponding Author
• Yong Mun Choi(Carbon Convergence Materials Research Center, Institute of Advanced Composite Materials, Korea Institute of Science and Technology (KIST))