doped (GDC) solid solutions have been considered as a promising materials for electrolytes in intermediate-temperature solid oxide fuel cells. In this study, the nano-sized GDC powder with average panicle size of 69nm was prepared by a high energy ball milling process and its sintering behavior was investigated. Heat-treatment at of nano-sized GDC powder mixture led to GDC solid-solution. The enhanced densification over 96% of relative density was obtained after sintering at for 2h. It was found that the sinterability of GDC powder could be significantly improved by the introduction of a high energy ball milling process

• 류성수 | Ryu Sung-Soo
• 김형태 | Kim Hyung-Tae