This paper deals with the phase analysis of bulk using spark plasma sintering process after ball milling. Mg and amorphous B powders were used as raw materials, and milled by planetary-mill for 9 hours at argon atmosphere. In order to confirm formation of phase, DTA and XRD were used. The milled powders were fabricated to bulk at the various temperatures by Spark Plasma Sintering. The fabricated bulk was evaluated with XRD, EDS, FE-SEM and PPMS. In the DTA result, reaction on formation of phase started at . This means that ball milling process improves reactivity on formation of phase. The MgO and FeB phases were characterized from XRD result. MgO and FeB were undesirable phases which affect formation of phase, and it's distribution could be confirmed from EDS mapping result. Spark Plasma Sintered sample for 5 min at was relatively densified and it's density and transition temperature showing super conducting property were and 21K.