Ti 분말 첨가가 TiO2 나노 분말의 성형성에 미치는 영향 KCI 등재

The Effect of Ti Powder addition on Compaction Behavior of TiO2 Nano Powder

  • 언어KOR
  • URLhttps://db.koreascholar.com/Article/Detail/2674
구독 기관 인증 시 무료 이용이 가능합니다. 4,000원
한국분말야금학회지 (Journal of Korean Powder Metallurgy Institute)
한국분말재료학회(구 한국분말야금학회) (Korean Powder Metallurgy Institute)
초록

The compaction response of nano powders with an addition of Ti powders prepared by magnetic pulsed compaction and subsequent sintering processes was investigated. All kinds of different bulk exhibited an average shrinkage of about 12% for different MPCed pressure and sintering temperature, which were approximately 50% lower than those fabricated by general process (20%) and a maximum density of around 92.7% was obtained for 0.8GPa MPCed pressure and sintering temperature. The addition of Ti powder induced an increase in the formability and hardness of the sintered . But the lower densities were obtained on sintering with addition of over 10 (wt%) Ti powder due to generation of crack during sintering. Subsequently it was verified that the optimum compaction pressure in MPC and sintering temperature were 0.8GPa and , respectively

저자
  • 박진섭
  • 김효섭
  • 이기석
  • 이정구
  • 이창규
  • 홍순직