Cobalt coated tungsten carbide-cobalt composite powder has been prepared through wet chemical reductionmethod. The cobalt sulfate solution was converted to the cobalt chloride then the cobalt hydroxide. The tungsten carbidepowders were added in to the cobalt hydroxide, the cobalt hydroxide was reduced and coated over tungsten carbidepowder using hypo-phosphorous acid. Both the cobalt and the tungsten carbide phase peaks were evident in the tungstencarbide-cobalt composite powder by X-ray diffraction. The average particle size measured via scanning electron micro-scope, particle size analysis was around 380 nm and the thickness of coated cobalt was determined to be 30~40 nm bytransmission electron microscopy.