In order to utilize waste wood chip for pavement, a polyurethane resin that is both eco-friendly and suitable for bindingwood chip was developed as the binder, and workability was examined through laboratory experiment for characteristicsof waste wood chip mixture using the polyurethane resin and through test pavement on the field. The new resin was aVOC reduction type free from plasticizer and solvent classified as endocrine-disrupting chemicals and environmentalhazardous substances, and NCO equivalents were set at 8, 9, 10 and 11% by modifying the polyisocyanate-polyol ratio.Laboratory experiment showed that polyurethane resin with NCO equivalent of 9% and 10% had excellent characteristicsas binder for waste wood chip. In the field experiment applying waste wood chip and polyurethane resin in the massratio of 1:0.8, tensile strength of the pavement system was about 30% higher than that using polyurethane resin currentlybeing sold, and permeability coefficient and elasticity thereof were the same as that using the resin currently being sold.Also, examination of compaction methods for waste wood chip pavement system showed that non-heating hand rollerand compactor had the problem of the “waste wood chip - resin mixture” sticking to the roller during the compaction but that heating hand roller had excellent workability and could achieve good planation surface relatively easily.