Titanium alloys are extensively used in high-temperature applications due to their excellent high strength andcorrosion resistance properties. However, titanium alloys are problematic because they tend to be extremely difficult-to-cut material. In this paper, the powder synthesis, spark plasma sintering (SPS), bulk material characteristics and machin-ability test of hybrid Ti2AlC ceramic bulk materials were systematically examined. The bulk samples mainly consistedof Ti2AlC materials with density close to theoretical value were synthesized by a SPS method. Random orientation andgood crystallization of the Ti2AlC was observed at 1100℃ for 10 min under SPS sintering conditions. Scanning electronmicroscopy results indicated a homogeneous distribution and nano-laminated structure of Ti2AlC MAX phase. The hard-ness and electrical conductivity of Ti2AlC were higher than that of Ti 6242 alloy at sintering temperature of 1000℃~1100℃. Consequently, the machinability of the hybrid Ti2AlC bulk materials is better than that of the Ti 6242 alloy formicro-EDM process of micro-hole shape workpiece.