Effect The effect of sintering additives (SiO2, Al2O3, Clay) on the mechanical characteristics of sintered zircon was investigated. 1 vol% of additives in zircon powder was was sintered at 120~1500˚C, the mechanical characteristics were measured, and microstructure analysis were was conducted. Al2O3 and clay additions increase the formation of monoclinic and tetragonal-ZrO2 formation. An addition of SiO2 addition suppressed the formation of tetragonal-ZrO2 formation., The A specimen sintered at 1400˚C showed the a density of 4.05 g/cm3 and the a microhardness of 1120 HV, respectively.