pp.389-393
Nano-sized TiO2-60 wt% SrO composite powders were synthesized by a sol-gel method using titanium isopropoxide and Sr(OH)2 · 8H2O as precursors. 3, -5, -7 wt%Ag spot-coated TiO2-60 wt% SrO composite powders were synthesized by a Ag electroless deposition method using TiO2-60 wt% SrO composite powders calcined at 1050˚C, which mainly exhibited the SrTiO3phase. However, a small number of rutile TiO2, Sr2TiO4 and SrO2 phases were also detected. In the Ag spot-coated powders synthesized by electroless deposition, nano-sized particles about 5-25 nm in diameter adhered to the TiO2-60 wt% SrO composite powders. The photocatalytic activity of Ag spot-coated TiO2-SrO and TiO2-SrO composite powders for degradation of phenol showed that all of TiO2-SrO composite powders were highly active under UV light irradiation. 7 wt%Ag spot-coated TiO2-60wt.%SrO composite powders had a relatively higher photocatalytic activity than did TiO2-SrO composite powders under visible light.