La doped CuO-ZnO-Al2O3 powders are prepared by sol-gel method with aluminum isopropoxide and primarydistilled water as precursor and solvent. In this synthesized process, the obtained metal oxides caused the precursor such ascopper (II) nitrate hydrate and zinc (II) nitrate hexahydrate were added. To improve the surface areas of La doped CuO-ZnO-Al2O3 powder, sorbitan (z)-mono-9-octadecenoate (Span 80) was added. The synthesized powder was calcined at varioustemperatures. The dopant was found to affect the surface area and particle size of the mixed oxide, in conjunction with thecalcined temperature. The structural analysis and textual properties of the synthesized powder were measured with an X-rayDiffractometer (XRD), a Field-Emission Scanning Electron Microscope (FE-SEM), Bruner-Emmett-Teller surface analysis (BET),Thermogravimetry-Differential Thermal analysis (TG/DTA), 27Al solid state Nuclear Magnetic Resonance (NMR) and transforminfrared microspectroscopy (FT-IR). An increase of surface area with Span 80 was observed on La doped CuO-ZnO-Al2O3powders from 25m2/g to 41m2/g.