Red phosphors Ca1-1.5xWO4:Eux3+ were synthesized with different concentrations of Eu3+ ions by using a solid-statereaction method. The crystal structure of the red phosphors was found to be a tetragonal system. X-ray diffraction (XRD) resultsshowed the (112) main diffraction peak centered at 2θ=28.71o, and the size of crystalline particles exhibited an overalldecreasing tendency according to the concentration of Eu3+ ions. The excitation spectra of all the phosphors were composedof a broad band centered at 275nm in the range of 230-310nm due to O2−→W6+ and a narrow band having a peak at 307nmcaused by O2−→Eu3+. Also, the excitation spectrum presents several strong lines in the range of 305-420nm, which areassigned to the 4f-4f transitions of the Eu3+ ion. In the case of the emission spectrum, all the phosphor powders, irrespectiveof Eu3+ ion concentration, indicated an orange emission peak at 594nm and a strong red emission spectrum centered at 615nm,with two weak lines at 648 and 700nm. The highest red emission intensity occurred at x=0.10mol of Eu3+ ion concentrationwith an asymmetry ratio of 12.5. Especially, the presence of Eu3+ in the Ca1-1.5xWO4:Eux3+ shows very effective use of excitationenergy in the range of 305-420nm, and finally yields a strong emission of red light.