논문 상세보기
pp.439-444
To compare the photocatalytic performances of titania for purification of waste water according to applied voltages and doping, TiO2 films were prepared in a 1.0 M H2SO4 solution containing NH4F at different anodic voltages. Chemical bonding states of F-N-codoped TiO2 were analyzed using surface X-ray photoelectron spectroscopy (XPS). The photocatalytic activity of the co-doped TiO2 films was analyzed by the degradation of aniline blue solution. Nanotubes were formed with thicknesses of 200-300 nm for the films anodized at 30 V, but porous morphology was generated with pores of 1-2 μm for the TiO2 anodized at 180 V. The phenomenon of spark discharge was initiated at about 98 V due to the breakdown of the oxide films in both solutions. XPS analysis revealed the spectra of F1s at 684.3 eV and N1s at 399.8 eV for the TiO2 anodized in the H2SO4-NH4F solution at 180 V, suggesting the incorporation of F and N species during anodization. Dye removal rates for the pure TiO2 anodized at 30 V and 180 V were found to be 14.0% and 38.9%, respectively, in the photocatalytic degradation test of the aniline blue solution for 200 min irradiation; the rates for the F-N-codoped TiO2 anodized at 30 V and 180 V were found to be 21.2% and 65.6%, respectively. From the results of diffuse reflectance absorption spectroscopy (DRS), it was found that the absorption edge of the F-N-codoped TiO2 films shifted toward the visible light region up to 412 nm, indicating that the photocatalytic activity of TiO2 is improved by appropriate doping of F and N by the addition of NH4F.