Trivalent cerium-ion-doped Y3(Al, Ga)5O12 nanoparticle phosphor nanoparticles were synthesized using the reversemicelle process. The Ce doped Y3(Al, Ga)5O12 particles were obtained from nitrate solutions dispersed in the nanosized aqueousdomains of a micro emulsion consisting of cyclohexane as the oil phase and poly(oxyethylene) nonylphenyl ether (Igepal CO-520) as the non-ionic surfactant. The crystallinity, morphology, and thermal properties of the synthesized Y3(Al, Ga)5O12:Ce3+powders were characterized by thermogravimetry-differential thermal analysis (TGA-DTA), X-ray diffraction analysis (XRD),scanning electron microscopy (SEM), and transmission electron microscopy. The crystallinity, morphology, and chemical statesof the ions were characterized; the photo-physical properties were studied by taking absorption, excitation, and emission spectrafor various concentrations of cerium. The photo physical properties of the synthesized Y3(Al, Ga)5O12:Ce3+ powders werestudied by taking the excitation and emission spectra for various concentrations of cerium. The average particle size of thesynthesized YAG powders was below 1µm. Excitation spectra of the Y3Al5O12 and Y3Al3.97Ga1.03O12 samples were 485nmand 475nm, respectively. The emission spectra of the Y3Al5O12 and Y3Al3.97Ga1.03O12 were around 560nm and 545nm,respectively. Y3(Al, Ga)5O12:Ce3+ is a red-emitting phosphor; it has a high efficiency for operation under near UV excitation,and may be a promising candidate for photonic applications.

• Kim, Min Yeong(School of Nano & Advanced Materials Engineering, Changwon National Univ)
• Bae, Dong-Sik( School of Nano & Advanced Materials Engineering, Changwon National Univ) | Bae, Dong-Sik