This present study deals with the effect of micro-alloying elements and transformation temperature on the correlation of microstructure and tensile properties of low-carbon steels with ferrite-pearlite microstructure. Six kinds of lowcarbon steel specimens were fabricated by adding micro-alloying elements of Nb, Ti and V, and by varying isothermal transformation temperature. Ferrite grain size of the specimens containing mirco-alloying elements was smaller than that of the Base specimens because of pinning effect by the precipitates of carbonitrides at austenite grain boundaries. The pearlite interlamellar spacing and cementite thickness decreased with decreasing transformation temperature, while the pearlite volume fraction was hardly affected by micro-alloying elements and transformation temperature. The room-temperature tensile test results showed that the yield strength increased mostly with decreasing ferrite grain size and elongation was slightly improved as the ferrite grain size and pearlite interlamellar spacing decreased. All the specimens exhibited a discontinuous yielding behavior and the yield point elongation of the Nb4 and TiNbV specimens containing micro-alloying elements was larger than that of the Base specimens, presumably due to repetitive pinning and release of dislocation by the fine precipitates of carbonitrides.

1. 서 론
 2. 실험 방법
 3. 실험 결과 및 고찰
  3.1 미세조직 변화
  3.2 인장 특성
 4. 결 론
 Acknowledgement
 References

• 이상인(서울과학기술대학교 신소재공학과) | Sang-In Lee
• 이지민(서울과학기술대학교 신소재공학과) | Ji-Min Lee
• 황병철(서울과학기술대학교 신소재공학과) | Byoungchul Hwang Corresponding author