Cellulose fibers were stabilized by treatment with an electron-beam (E-beam). The properties of the stabilized fibers were analyzed by scanning electron microscopy, Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, and thermogravimetric analysis. The E-beam-stabilized cellulose fibers were carbonized in N2 gas at 800°C for 1 h, and their carbonization yields were measured. The structure of the cellulose fibers was determined to have changed to hemicellulose and cross-linked cellulose as a result of the E-beam stabilization. The hemicellulose decreased the initial decomposition temperature, and the cross-linked bonds increased the carbonization yield of the cellulose fibers. Increasing the absorbed E-beam dose to 1500 kGy increased the carbonization yield of the cellulose-based carbon fiber by 27.5% upon exposure compared to untreated cellulose fibers.

• Min Il Kim(Department of Fine Chemical Engineering and Applied Chemistry, Chungnam National University, Daejeon 34134, Korea)
• Mi-Seon Park(Department of Fine Chemical Engineering and Applied Chemistry, Chungnam National University, Daejeon 34134, Korea)
• Young-Seak Lee(Department of Fine Chemical Engineering and Applied Chemistry, Chungnam National University, Daejeon 34134, Korea) Corresponding Author