Unidirectionally solidified TiAl alloys were prepared by optically-heated floating zone method at growth rates of 10 to 70 mm/h in flowing argon. The microstructures and tensile properties of these crystal bars were found to depend strongly on the growth rate and alloy composition. TiAl alloys with composition of 47 and 50 at.%Al grown under the condition of 10 mm/h showed Ti3Al(α2)/TiAl(γ) layer structures similar to single crystals. As the growth rate increased, the alloys with 47 and 50 at.%Al compositions showed columnar-grain structures. However, the alloys fabricated under the condition of 10 mm/ h had a layered structure, but the alloy with increased growth rate consisted of γ single phase grains. The alloy with a 53 at.%Al composition showed a γ single phase regardless of the growth rate. Room-temperature tensile tests of these alloys revealed that the columnar-grained material consisting of the layered structure showed a tensile ductility of larger than 4 % and relatively high strength. The high strength is caused by stress concentration at the grain boundaries; this enhances the secondary slip or deformation twinning across the layered structure in the vicinity of the grain boundaries, resulting in the appreciable ductility.

• Chang-Suk Han(Department of ICT Automotive Engineering, Hoseo University, Chungnam 31702, Republic of Korea) Corresponding author
• Sang-Wook Kim(Department of Nanobiotronics, Hoseo University, Chungnam 31702, Republic of Korea)