논문 상세보기
Development of forward osmosis (FO) membranes with high salt selectivity is a essential issue to realize the FO technology. To improve salt selectivity of the FO membrane, a polyamide thin film composite FO membrane was fabricated by the interfacial polymerization method using aromatic hydrocarbon organic solvents on polyacrylonitrile (PAN) supports. The aromatic hydrocarbon organic solvent accelerated amine diffusion rate toward the organic phase and the subsequent reaction, which can improve membrane performance by fabricating a thin and highly dense basal PA layer. As a result, the prepared FO membrane showed ~1.7 times higher flux and ~4.5 times higher salt selectivity compared to HTI-CTA commercial membrane with 1.0 M NaCl draw solution and DI water feed solution in FO mode.