Every year, 1.1 million tons of rice-hull are produced in South Korea by the by-product in pounding rice. But they has mainly been utilized as a fuel, agricultural compost and moisture proofs. So, it's very valuable to use waste rice-hull for activated carbon manufacture.
SiO2 content was the highest among inorganics in rice-hull. Therefore, the SiO2 extraction experiments were carried out under the various conditions of pH 9 to 14, reaction time from 2 to 24 hrs and various temperature of 20 to 100℃.
The results showed that increase in pH and temperature enhanced SiO2 extraction from the carbonized rice-hull. The surface area of the carbonized rice-hull indicating activated carbon adsorption capacity was very small as 178∼191 ㎡/g at first. However, it was increased to 610∼675 ㎡/g when extracted in alkali solution at 100℃. When the mixing rate of carbonized rice-hull and NaOH was 1:1.5, iodine No. and surface area of activated rice-hull during 10 min at 700℃ were 1,650 ㎎/g and 1837 ㎡/g, respectively. Subsequently, an activated carbon with specific surface area of 1,300∼1,900㎡/g was manufactured in a short contact time of 10∼30 min with a mixing rate of 1:1.5 in carbonized rice-hull and NaOH, and iodine No. and specific surface area increased as the amount of SiO2 removal increased.