(1) Using high-frequency induction heating sintering and spark plasma sintering method, the densification of WC-Ni hard materials was accomplished using ultra fine power of Ni and WC. (2) Nearly fully dense WC-Ni could be obtained within 1 min. (3) Relative density and mechanical properties of WC-Ni obtained by HFIHS were high than those obtained by SPS. And WC grain size made by HFIHS was smaller than that made by SPS. (4) The fracture toughness and hardness values of WC-8Ni, WC-10Ni, and WC-12Ni made by HFIHS were , respectively for 60MPa and an induced current for 90% output of total capacity, 15KW. (5) The fracture toughness and hardness values of WC-8Ni, WC-10Ni, and WC-12Ni made by SPS were , respectively for 60MPa and the electric current of 2500 A

• Hwan-Cheol Kim(Department of Materials Engineering, Chonbuk National University)
• Dong-Young Oh(Department of Materials Engineering, Chonbuk National University)
• In-Jin Shon(Department of Materials Engineering, Chonbuk National University)