Various surface colors are predicted and implemented using the interference color generated by controlling the thickness of nano-level diamond like carbon (DLC) thin film. Samples having thicknesses of up to 385 nm and various interference colors are prepared using a single crystal silicon (100) substrate with changing processing times at low temperature by plasma-enhanced chemical vapor deposition. The thickness, surface roughness, color, phases, and anti-scratch performance under each condition are analyzed using a scanning electron microscope, colorimeter, micro-Raman device, and scratch tester. Coating with the same uniformity as the surface roughness of the substrate is possible over the entire experimental thickness range, and more than five different colors are implemented at this time. The color matched with the color predicted by the model, assuming only the reflection mode of the thin film. All the DLC thin films show constant D/G peak fraction without significant change, and have anti-scratch values of about 19 N. The results indicate the possibility that nano-level DLC thin films with various interference colors can be applied to exterior materials of actual mobile devices.

Abstract
1.서 론
2. 실험방법
3. 결과 및 고찰
4.결 론
References

• 박새봄(트인로드(주)) | Saebom Park (Turinroad Co. Ltd.)
• 김광배(서울시립대학교 신소재공학과) | Kwangbae Kim (Department of Materials Science and Engineering, University of Seoul)
• 김호준(서울시립대학교 신소재공학과) | Hojun Kim (Department of Materials Science and Engineering, University of Seoul)
• 김치환(트인로드(주)) | Chihwan Kim (Turinroad Co. Ltd.)
• 최현우(트인로드(주)) | Hyun Woo Choi (Turinroad Co. Ltd.)
• 송오성(서울시립대학교 신소재공학과) | Ohsung Song (Department of Materials Science and Engineering, University of Seoul) Corresponding author