In this study, microstructural characteristics and constituent elements of fiberglass splint and cast are examined using a scanning electron microscope and an energy dispersive X-ray spectrometer. As observed by the scanning electron microscope, fiberglass splint and cast had a porous structure with many bundles of fiberglass textures well assembled. Spaces between bundles of the fiberglass splint are triangular or elliptical shaped and the long-axis diameter is measured at about 1 mm. The thickness of fiber bundles covered with plaster is measured at 600 μm and the diameter of a single strand of fiberglass is up to 10 μm. The thickness of the fiberglass bundle of the fiberglass splint is measured at about 700 μm. Spaces between bundles are formed in the shape of triangles with gentle edges and long-axis diameter of up to 1.4 mm, which is larger than that of the splint. The thickness of a single strand of fiberglass of the plaster-coated cast is 11.5 μm, which is thicker than that of fiberglass of the splint. As a result of analyzing constituent elements of the fiberglass cast and the splint with an energy dispersive X-ray spectrometer, Ca, Si, and Al components are identically detected. This result shows that the fiberglass cast has a smoother surface with hardened plaster than the fiberglass splint. The thickness of the fiberglass bundle and the thickness of a single strand of the fiberglass are also larger than those of the fiberglass splint.

Abstract
1. Introduction
2. Materials and Methods
    2.1. Experimental Materials
    2.2. Scanning Electron Microscopy
    2.3. Energy Dispersive X-ray Spectrometry
3. Results
4. Discussion
5. Conclusion
References

• Joo Hyun Ham(Department of Health Counselling and Welfare, Hanseo University)
• Han Suk Jung(Department of Chiropractic Hanseo University) Corresponding author