This study was to develop a piston rod made of SiC by applying a sintering treatment after press molding in order to replace the imported piston rod used in the past. As a result of evaluating the mechanical properties of the developed piston rod, the following conclusions were obtained. The surface roughness value of the piston rod made of silicon carbide was 0.950Ra, and the surface Vickers hardness value was 19.94GPa. As a result of XRD analysis of the surface of the prototype piston rod, the main crystalline phase was 6H-SiC, and the crystalline phases of 4H-SiC and α-SiC were existed. In addition, a trace amount of SiC was detected. As a result of SEM observation of the piston rod surface of the prototype, a number of large porosity were observed. As a result of measuring the surface hardness of the piston rod made of SiC, it showed 70% of the physical properties compared to imported products.