This research investigated the effect of Si addition on the microstructure, mechanical properties, electric and thermal conductivity of as-extruded Al 6013 alloys. As the content of Si increased, the area fraction of the second phase increased. As the Si content increased, the average grain size decreased remarkably, from 182 (no Si addition) to 142 (1.5Si), 78 (3.0Si) and 77 μm (4.5Si) due to dynamic recrystallization by the dispersed second particles in the aluminum matrix during the hot extrusion. As the Si content increased, the yield strength and ultimate tensile strength increased. The maximum values of yield strength and ultimate tensile strength were 224 MPa and 103 MPa for the 6013-4.5Si alloy. As the amount of Si added increased, the electrical and thermal conductivity decreased. The electrical and thermal conductivity of the Al6013-4.5Si alloy were 44.0% IACS and 165.0 W/mK, respectively. The addition of Si to Al 6013 alloy had a significant effect on its thermal conductivity and mechanical properties.

Abstract
1. Introduction
2. Experimental Procedure
3. Results and Discussion
4. Conclusion
Acknowledgments
References

• Hyo-Sang Yoo(Automotive Materials & Components R&D Group, Korea Institute of Industrial Technology)
• Yong-Ho Kim(Automotive Materials & Components R&D Group, Korea Institute of Industrial Technology)
• Byoung-Kwon Lee(Automotive Materials & Components R&D Group, Korea Institute of Industrial Technology)
• Eun-Chan Ko(Automotive Materials & Components R&D Group, Korea Institute of Industrial Technology)
• Hyeon-Taek Son(Automotive Materials & Components R&D Group, Korea Institute of Industrial Technology) Corresponding author