In this paper, we report and discuss the semi-permanently hydrophilic (SPH) treatment of polyester fabric using plasma polymerization and oxidation based on atmospheric pressure dielectric barrier discharge (APDBD) technology. SiOxCy (-H) was coated on polyester fabric using Hexamethylcyclotrisiloxane (HMCTSO) as a precursor, and then plasma oxidation was performed to change the upper layer of the thin film to SiO2-like. The degradation of hydrophilicity of the SPH polyester fabrics was evaluated by water contact angle (WCA) and wicking time after repeated washing. The surface morphology of the coated yarns was observed with scanning electron microscopy, and the presence of the coating layer was confirmed by measuring the Si peak using energy dispersive x-ray spectroscopy. The WCA of the SPH polyester fabric increased to 50 degrees after 30 washes, but it was still hydrophilic compared to the untreated fabric. The decrease in hydrophilicity of the SPH fabric was due to peeling of the SiOxCy(-H) thin film coated on polyester yarns.

Abstract
1. Introduction
2. Experimental
    2.1. Materials
    2.2. Plasma polymerization and oxidation
    2.3. Wetting measurement
    2.4. Morphology studies
3. Results and Discussion
    3.1. Water contact angle and wetting
    3.2. Morphology
4. Conclusions
References

• Se Hoon Shin(Department of Materials Science and Engineering, Hanbat National University)
• Yoon Kee Kim(Department of Materials Science and Engineering, Hanbat National University) Corresponding author