One-dimensional MgO nanostructures with various morphologies were synthesized by a thermal evaporation method. The synthesis process was carried out in air at atmospheric pressure, which made the process very simple. A mixed powder of magnesium and active carbon was used as the source powder. The morphologies of the MgO nanostructures were changed by varying the growth temperature. When the growth temperature was 700 °C, untapered nanowires with smooth surfaces were grown. As the temperature increased to 850 °C, 1,000 °C and 1,100 °C, tapered nanobelts, tapered nanowires and then knotted nanowires were sequentially observed. X-ray diffraction analysis revealed that the MgO nanostructures had a cubic crystallographic structure. Energy dispersive X-ray analysis showed that the nanostructures were composed of Mg and O elements, indicating high purity MgO nanostructures. Fourier transform infrared spectra peaks showed the characteristic absorption of MgO. No catalyst particles were observed at the tips of the one-dimensional nanostructures, which suggested that the one-dimensional nanostructures were grown in a vapor-solid growth mechanism.

• 김남우(동의대학교 신소재공학부) | Nam-Woo Kim (Division of Advanced Materials Engineering, Dong-Eui University, Busan 47340, Republic of Korea)
• 김진수(동의대학교 신소재공학부) | Jin-Su Kim (Division of Advanced Materials Engineering, Dong-Eui University, Busan 47340, Republic of Korea)
• 이근형(동의대학교 신소재공학부) | Geun-Hyoung Lee (Division of Advanced Materials Engineering, Dong-Eui University, Busan 47340, Republic of Korea) Corresponding author