The effect of Li2O addition on precipitation behavior of uranium in LiCl-KCl-UCl3 has been investigated in this study. 99.99% LiCl-KCl eutectic salt is mixed with 10wt% UCl3 chips at 550°C in the Pyrex tube in argon atmosphere glove box, with 10 ppm O2 and 1 ppm H2O. Then, Li2O chunks are added in mixed LiCl-KCl-UCl3 and the system has been cooled down to room temperature for 10 hours to form enough UO2 particles in the salt. The solid salt has been taken out from the glove box, and cut into three sections (top, middle and bottom) by low-speed saw for further microscopic analysis. Three pieces of solid salt are dissolved in deionized water at room temperature and the solution is filtered by a filter paper to collect non-dissolved particles. The filter paper with particles is baked in vacuum oven at 120°C for 6 hours to evaporate remaining moisture from the filter paper. Further analysis was performed for the powder remaining on the filter paper, and periphery of the powder (cake) on the filter paper. Scanning electron microscopy (SEM), electron diffraction spectroscopy (EDS), and X-ray powder diffraction (XRD) are adopted to analysis the characteristic of the particles. From SEM analysis, the powders are consisted of small particles which have 5 to 10 m diameter, and EDS analysis shows they are likely UO2 with 23 at. % of uranium and 77 at. % oxygen. Cake is also analyzed by SEM and EDS, and needle like structures are widely observed on the particle. The length of needle is distributed from 5 to 20 m, and it has 6 to 10 at. % of chlorine, which are not fully dissolved into deionized water at room temperature. From XRD analysis, the particles show the peak position of UO2, and the result is well matched with the SEM-EDS results. We are planning to add more Li2O in the system for fully reacting uranium in UCl3, and compare the results to find the effect of Li2O concentration on UO2 precipitation.

• Taeho Kim(Korea Atomic Energy Research Institute (KAERI)) Corresponding author
• Su Jeong Heo(Korea Atomic Energy Research Institute (KAERI))
• Dalsung Yoon(Korea Atomic Energy Research Institute (KAERI))
• Seungwoo Paek(Korea Atomic Energy Research Institute (KAERI))
• Chang Hwa Lee(Korea Atomic Energy Research Institute (KAERI))