Uniformity of Droplet of Eutectic NaCl-MgCl2 System for Corrosion Test of Coating Layer
- 언어ENG
- URLhttps://db.koreascholar.com/Article/Detail/431494
p.488
Corrosion-related challenges remain a significant research topic in developing next-generation Molten Salt Reactors (MSRs). To gain a deeper understanding of preventing corrosion in MSRs, previous studies have attempted to improve the corrosion resistance of structural alloys by coating surfaces such as alumina coating. To conduct a corrosion test of coating alloys fully immersed in molten salt, it’s important to ensure that the coating application process is carefully carried out. Ideally, coating all sides of the alloy is necessary to avoid gaps like corners of the alloy, while only applying a one-sided coating alloy can lead to galvanic corrosion with the base metals. Using the droplet shape of eutectic salt applied to only one side of the coating alloy would avoid these problems in conventional corrosion immersion tests, as corrosion would occur solely on the coating surface. Although the droplet method for corrosion tests cannot fully replicate corrosion in the MSRs environment, it offers a valuable tool for comparing and evaluating the corrosion resistance of different coating surfaces of alloys. However, the surface area is important due to the effect of diffusion in the corrosion of alloy in molten salt environments, but it is difficult to unify in the case of droplet tests. Therefore, understanding the droplet-alloy properties and corrosion mechanism is needed to accurately predict and analyze these test systems’ behavior highlighting unity for corrosion tests of different coating surfaces of alloys. To analyze the molten salt droplet behavior on various samples, pelletized eutectic NaCl-MgCl2 was prepared as salt and W-, Mo-coating, and base SS316 as samples. At room temperature, the same mass of pelletized eutectic NaCl-MgCl2 was placed on different samples under an argon atmosphere and heated to a eutectic point of 500°C in a furnace. After every hour, the molten droplets were hardened by rapid cooling at room temperature outside the furnace. The mass loss of salts and the contact area of the samples were measured by mass balance and SEM. The shape, surface area to volume ratio, and evaporation of the droplets of NaCl-MgCl2 per each coating sample and hour were analyzed to identify the optimal mass to equalize the contact coating surface of alloys with salts. Furthermore, We also analyzed whether their results reached saturation of corrosion products through ICP-MS. This will be significant research for the uniformity of the liquid-drop shape corrosion test of the coating sample in molten eutectic salts.