Evaluation of Physical Properties of Polyurethane Resin for Wound Covering according to PTMG, DMBA Application KCI 등재

PTMG, DMBA 적용에 따른 창상피복 폴리우레탄 수지의 물리적 특성 평가

  • 언어ENG
  • URLhttps://db.koreascholar.com/Article/Detail/404524
구독 기관 인증 시 무료 이용이 가능합니다. 4,000원
한국응용과학기술학회지 (The Korean Society of Applied Science and Technology)
한국응용과학기술학회(구 한국유화학회) (The Korean Society of Applied Science and Technology (KSAST))
초록

In this study, the polyurethane resin was synthesized by applying PTMG and DMBA of different composition ratios for the synthesis of water-dispersible polyurethane used in wound coating resin. The varying properties of the synthesized water-dispersible polyurethane were measured through tensile strength, elongation, and abrasion resistance analysis. As for the tensile strength measurement result according to the PTMG content, the sample with the highest reaction molar ratio was measured as 1.08 kgf/mm2 and the elongation was measured as 520%. As for the tensile strength result according to the DMBA content, the sample with the highest reaction molar ratio was measured as 0.51 kgf/mm2, and the elongation was measured as 435%. The degree of surface destruction by the abrasion resistance measurement was visually confirmed through SEM.

목차
Abstract
1. Introduction
2. Experiment
    2.1. Reagent/analysis equipment andsynthesis method
3. Results and Discussion
    3.1. Analysis of mechanical properties(tensile strength, elongation,adhesive strength)
4. Conclusion
References