A series of amphiphilic block copolymers consisting of hydrophobic poly(methyl methacrylate) (PMMA) and poly(polyethylene glycol methyl ether methacrylate) (PPEGEMA) were synthesized by Cu based ATRP and utilized as an additive to prepare asymmetric ultrafiltration (UF) membranes by non-solvent induced phase separation (NIPS) with PVDF. Obtained PVDF based UF membranes gave in-situ hydrophilic surfaces on the hydrophobic PVDF matrix because of strong compatibility PMMA block segment to PVDF and the hydrophilicty of PPEGMA block segment to the non-solvent (water), which showed improved water flux in comparison to neat PVDF UF membrane.

Amine functionalized polysulfone (PSf) based ultrafiltration (UF) membranes were prepared by non-solvent induction phase separation method (NIPS) with reactive PSf (matrix) and polyehtyleneimine (PEI) (additive), where PEI was reacted in dope solution to give surface modified PSf-UF membrane. Unreacted PEI might be worked as a forming agent during NIPS, however it was not much affected to the pore structures. Obtained membranes showed enhanced hydrophilic property on the membrane, which increased the water flux without loss of the rejection rate of PEO (100 K).

유가금속 및 희소금속의 수요가 많아짐에 따라 제련공정에서 발생하는 황산 용액 내의 유가금속 및 희소금속을 회수하여 사용하는 방향의 연구가 진행되고 있다. 이에 황산용액 내의 희소금속 및 유가금속을 분리하기 위해서는 내산성이 뛰어난 나노분리막이 필요하다. 따라서 본 연구에서는 우수한 내산성을 가진 방향족 폴리아미드 나노여과막을 제조하였으며 제조된 분리막의 나노여과 특성과 내산성 및 내열성을 평가하였다.

역삼투 공정은 에너지 효율의 증가로 해수담수화에서 많이 사용되고 있는 공정이다. 보론은 해수에서 대개 4∼5 mg/L의 농도로 존재하며, pH 8.2에서 B(OH)3로 76%, B(OH)4 -로 12%, 나머지 11%는 복합체와 금속 이온을 이룬 구조로 존재하고 있다. 이러한 구조로 인해 역삼투 후에도 보론 한계기준보다 높은 수치로 남아 있어 효과적으로 제거할 수 있는 공정이 필요하다. 본 연구에서는 N-methyl-D-glucamine (NMDG)이 포함된 첨가제를 이용하여 역삼투막을 제조 하였으며, 제조된 막의 성능을 평가하였다.