In this study, the diffusion behaviors of C and Co in liquid phase sintering of WC-Co system were investigated whether these two components diffused in the same direction in case of having opposite gradient each other with not being phase. The green compacts with controlled compositions in not being of phase and gradient composition which one is WC-5Co-1.2%C, the other is WC-XCo-0.2%C (where X = 5, 10, 15, 20, 25) were sintered at and and then the diffusion behaviors of C and Co were investigated by analyses of compositional change, also determined for microstructure and microhardness. Also, same testing was carried out on the specimens with dual layers sintered in upright and reverse positions to evaluate the effect of gravity on the diffusion in liquid Co. From the results of this study, we can find the fact that the direction of diffusion for C and Co in WC-Co system during liquid phase sintering was different and the effect of gravity for the liquid was insignificant. Also other physical properties were changed on the diffusion of elements.

In a manufacturing technique of the sintered filter, pressureless sintering method has good permeability, it is not need the binder and lubricant used on compacting process, so it has little contamination and it is easy to control the pore size and shape but the mechanical strength is low relatively and it is difficult that parts of complicate form are manufactured. In the case of manufacturing the filter by press and sintering method, in order to be satisfactory characteristic of un-pressed filter, in this study sintered metal filter fabricated by using 30-40mesh stainless steel 316L powder and additive agents. Porosity and structure of pores, permeability and mechanical strength of the sintered filter were investigated with the variation sintering conditions. Porosity was nearly constant about , density, permeability and mechanical strength were changed markedly with quantity of additive materials and sintering conditions.

The spherical particles of CeO2/SiO2 composite powder with narrow-size distribution and pure phase particles were synthesized by ultrasonic spray pyrolysis method from aqueous cerium sulfate solution. The resulting composite powder was characterized by X-ray diffraction, scanning electron microscopy, transmittance electron microscopy, in-vitro sun protect factor, and BET surface area analysis. The concentration of cerium sulfate was tested to vary the particle size from 3.40×10-3 to 1.02×10-2mol/cm3 to study concentration effect of starting material. The average particle size from the 3.40×10-3mol/cm3 concentration was found to be slightly smaller than that from the 1.02×10-2mol/cm3 concentration, because of the relation between the droplet size and the concentration of the starting material solution