High Pressure High Temperature (HPHT) treatment can significantly change the color of diamonds. We studied the variation of the optical properties according to the nitrogen arrangement in natural brown diamonds of various types (type IaAB, type IaB, type IaA > B, type IaA< B, IaA = B) after HPHT treatment. The diamonds with different arrangements of nitrogen were annealed at temperatures in the range 1700-1800˚C under a stabilizing pressure of 5 GPa. HPHT treated samples were analyzed using UV-Vis-NIR, FT-IR, and PL spectroscopy. The absorption and luminescence spectra were measured to compare the variations of nitrogen arrangement in the natural brown diamonds before and after HPHT treatment. After HPHT treatment, the brown coloration in all types of diamonds was reduced and a decrease in the peaks related to the A-aggregate of nitrogen was more predominant than the B-aggregate. Furthermore, the peaks related to N3 (415.4 nm), H4 (496.4 nm), and platelet decreased and the peaks related to H3 (503.2 nm) and G-band increased after HPHT treatment. In conclusion, spectroscopic analysis of natural brown diamonds after HPHT treatment showed that a yellow color was produced by absorption in the H3 centers and a green color was generated by interaction between absorptions of the H3 and H2 centers.

보석광물로서 거래되는 천연 다이아몬드의 타입별 분포와 각 타입별 다이아몬드의 광학적 특성을 조사하여 다이아몬드의 타입과 광학적 특성 사이에 존재하는 관련성을 관찰하였다. 조사된 다이아몬드 시료의 모두가 타입la으로 분류되었는데 A집합체만을 가지는 타입IaA, B집합체만을 가지는 타입IaB, 그리고 A집합체와 B집합체를 동시에 함께 가지는 타입IaAB로 세분되었다. A집합체 보다 B집합체가 상대적으로 증가할수록 N3센터의 증가, 청색 형광반응의 증가 및 응력 현상의 불규칙성이 증가하는 현상이 관찰되었다. 이와 같은 다이아몬드의 특성 변화는 A집합체에서 B집합체로 변화하는 질소의 집합화 과정에서 부수적 으로 발생하는 N3센터와 전위의 형성에 의한 광학적 현상과 일치하므로 다이아몬드 타입과 광학적 특성사이에 밀접한 관련성이 존재하는 것을 추론된다.