In this work, the correlation between the pore characteristics of activated carbon (AC) and the adsorption/desorption characteristics of evaporated fuel was studied. AC was prepared by various physical re-activation methods using coconut-derived commercial AC. Pore characteristics of the re-activated AC were investigated using N2/ 77 K adsorption isotherms. The structural characteristics of the AC were observed by X-ray diffraction and Raman spectroscopy. The butane working capacity was observed according to ASTM D5228. From the results, the specific surface area and total pore volume of the ACs were determined to be 1380–2040 m2/g and 0.60–0.96 cm3/g, respectively. It was also observed that various pore size distributions were found to be dependent on the functions of the activation method and time. A close relationship between butane activity/ retentivity and micropore/mesopore volumes was found. In addition, it was inferred that the volume fraction of micropores and sub-mesopores with diameters between 1.5 and 3.0 nm primarily controls butane activity.

In this study, we prepared ACFs with a high specific surface area from various precursors (rayon, pitch, and oxidized polyacrylonitrile-based fibers) by a steam-activation technique and investigated the effects of the micropore and mesopore fraction on 2-CEES adsorption behaviors. The activation time was precisely controlled so that the activation yield was in the range of 35–40% to ensure the mechanical properties of the ACFs. The N2 adsorption isotherm characteristics at 77K were confirmed by Brunauer–Emmett–Teller, Barrett–Joyner–Halenda and non-local density functional theory equations. The adsorption capacities of the ACF were measured by breakthrough experiments in the gas phase (750 μg/mL of 2-CEES in N2 flow). The removal efficiency of the ACFs was evaluated and compared with that of AC. From the results, specific surface areas and total pore volume of the ACF were determined to be 1380–1670 m2/g and 0.61–0.82 cm3/g, respectively. It was also observed that various pore characteristics of ACF were found to be dependent on crystallite structure of each precursor. The break through time (C/C0 = 0.10) was in the order of Oxi-Pan-H-9-2 < Saratoga AC < Rayon-H-9-3 < Pitch-H-9-4. This indicates that 2-CEES adsorption capacity could be a function not only of specific surface area or total pore volume, but also of sub-mesopore volume fraction in the range of 1.5–2.5 nm of adsorbents.