Concrete structures must maintain their shielding abilities and structural integrity over extended operational periods. Despite the widespread use of dry storage systems for spent nuclear fuel, research on the properties of deteriorated concrete and their impact on structural performance remains limited. To address this significant research gap, static and dynamic material testing was conducted on concrete specimens carefully extracted from the outer wall of the High-flux Advanced Neutron Application ReactOr (HANARO), constructed approximately 30 years ago. Despite its age, the results reveal that the concrete maintains its structural integrity impressively well, with static compression tests indicating an average compressive strength exceeding the original design standards. Further dynamic property testing using advanced high-speed material test equipment supported these findings, showing the consistency of dynamic increase factors with those reported in previous studies. These results highlight the importance of monitoring and assessing concrete structures in nuclear facilities for long-term safety and reliability.

In concrete structures exposed to chloride environments such as seashore structures, chloride ions penetrate into the concrete. Chlorine ions in concrete react with cement hydrates to form Friedel’s salt and change the microstructure. Changes in the microstructure of concrete affect the mechanical performance, and the effect varies depending on the concentration of chloride ions that have penetrated. However, research on the mechanical performance of concrete by chloride ion penetration is lacking. In this study, the effect of chloride ion penetration on the mechanical performance of dry cask concrete exposed to the marine environment was investigated. The mixture proportion of self-compacting concrete is used to produce concrete specimens. CaCl2 was used to add chlorine ions, and 0, 1, 2, and 4% of the binder in weight were added. To evaluate the mechanical performance of concrete, a compressive strength test, and a splitting tensile strength test were performed. The compressive strength test was conducted through displacement control to obtain a stress-strain curve, and the loading speed was set to 10 με/sec, which is the speed of the quasi-static level. The splitting tensile strength test was performed according to KS F 2423. As a result of the experiment, the compressive strength increased when the chloride ion concentration was 1%, and the compressive strength decreased when the chlorine ion concentration was 4%. The effect of the chloride ion concentration on the peak strain was not shown. In order to present a stress-strain curve model according to the chloride ion concentration, the existing concrete compressive stress-strain models were reviewed, and it was confirmed that the experimental results could be simulated through the Popovics model.

In this study, the mechanical property and durability of improved bond performance mortar shotcrete was investigated. Mortar shotcrete was prepared by replacing coarse aggregate with 100% fine aggregate in the shotcrete mixture proportion proposed in the road construction standard specification. OPC, GGBFS and anhydrite were used as binders, and polymer powder was substituted for 1% and 2% of binder for improving bond property. From the experimental results, it was found that the compressive strength decreased with increasing polymer addition, but the bond strength increased. The addition of polymer to mortar shotcrete also reduced the drying shrinkage and improved the resistance to carbonation. Initial hydration heat of mortar shotcrete decreased with the addition of polymer, and it was judged that the initial compressive strength decreased.