Spinnable mesophase pitch precursor containing more than 98% mesophase content was successfully prepared from FCC-DO (fluid catalytic cracking-decant oil) without hydrogenation or catalytic reaction. The preparation method involved thermal condensation, vacuum treatment, and annealing treatment. Petroleum mesophase pitch-based carbon fibers are produced by melt spinning of pitch precursors, followed by stabilization and carbonization. The resulting carbon fiber exhibited good mechanical performances up to tensile strength of 2.1 GPa and tensile modulus of 212 GPa, with strain-to-failure higher than 1.0%. These properties ensuring that the automotive grade carbon fibers can be successfully prepared from FCC-DO derived petroleum mesophase pitches through the cost-competitive processes.

Pyrolyzed fuel oil (PFO) and coal tar was blended in the feedstock to produce pitch via thermal reaction. The blended feedstock and produced pitch were characterized to investigate the effect of the blending ratio. In the feedstock analysis, coal tar exhibited a distinct distribution in its boiling point related to the number of aromatic rings and showed higher Conradson carbon residue and aromaticity values of 26.6% and 0.67%, respectively, compared with PFO. The pitch yield changed with the blending ratio, while the softening point of the produced pitch was determined by the PFO ratio in the blends. On the other hand, the carbon yield increased with increasing coal tar ratio in the blends. This phenomenon indicated that the formation of aliphatic bridges in PFO may occur during the thermal reaction, resulting in an increased softening point. In addition, it was confirmed that the molecular weight distribution of the produced pitch was associated with the predominant feedstock in the blend.

This research considers the effect of added mesophase pitch (MP) as an additive during the pitch synthesis reaction of pyrolyzed fuel oil (PFO). Two effects are generated by adding MP. One is an enhancement of thermal stability due to the high thermal property of the additive; the other is that the volatile compounds that were removed by vaporization of PFO during the thermal reaction can participate in the pitch synthesis reaction (PFO→pitch) more efficiently. The effect differs according to the amount of the additive. When the amount of the additive is less than 7 wt%, the first effect is dominant, whereas the second effect is dominant when the additive amount exceeds 10 wt%.

Needle coke is an important material for graphite electrodes. Delayed coking is used to produce needle coke. Producing good quality needle coke is not simple because it is a multi-parameter controlled process. Apart from that, it is important to understand the mechanism responsible for the delayed coking process, which involves mesophase formation and uniaxial rearrangement. Temperature and pressure need to be optimized for the different substances in every feedstock. Saturate hydrocarbon, aromatic, resin and asphaltene compounds are the main components in the delayed coking process for a low Coefficient Thermal Expansion value. In addition, heteroatoms, such as sulphur, oxygen, nitrogen and metal impurities, must be considered for a better graphitization process that prevents the puffing effect and produces better mesophase formation.