Abstract In this study, micro-defects on/in carbon fibers were modified by irradiation with an electron beam, which improved the mechanical strength of single carbon fibers. The electron beam irradiation was 10 kGy (using a 1.5 MeV accelerator in the air). The total doses ranged from 100 to 500 kGy. The tensile strength of the single carbon fiber was measured using a universal testing machine. The micro-defects on the fiber surface were observed with scanning electron microscopy and atomic force microscopy, and those in the fiber were evaluated by Raman spectroscopy. In conclusion, the electron beam treatment produced changes in the micro-defects on/in the carbon fibers, resulting in up to 14% improvement in the tensile strength of single carbon fiber.

Biodegradable epoxy (B-epoxy) was prepared from diglycidyl ether of bisphenol A and epoxidized linseed oil. The mechanical properties of B-epoxy composites reinforced with multi-walled carbon nanotubes (MWCNTs/B-epoxy) were examined by employing dynamic mechanical analysis, critical stress intensity factor (KIC) tests, and impact strength tests. The electromagnetic interference shielding effectiveness (EMI-SE) of the composites was evaluated using reflection and absorption methods. Mechanical properties of MWCNTs/B-epoxy were enhanced with an increase in the MWCNT content, whereas they deteriorated when the MWCNT content was >5 parts per hundred resin (phr). This can likely be attributed to the entanglement of MWCNTs with each other in the B-epoxy due to the presence of an excess amount of MWCNTs. The highest EMI-SE obtained was ~16 dB for the MWCNTs/B-epoxy composites with a MWCNT content of 13 phr at 1.4 GHz. The composites (13 phr) exhibited the minimum EMI-SE (90%) when used as shielding materials at 1.4 GHz. The EMI-SE of the MWCNTs/B-epoxy also increased with an increase in the MWCNT content, which is a key factor affecting the EMI-SE.