In this paper, we designed and fabricated the Electro-Magnetic (EM) wave absorber for wireless LAN by using Amorphous and CPE. The material constants and the absorption properties were measured for the samples containing 50 %, 60 %, and 70 % weight fraction of Amorphous. Moreover, the EM wave absorption abilities were simulated for the EM absorbers in different thicknesses by adopting the measured permittivity and permeability, and then the EM wave absorber was fabricated based on the simulated design values. As a result, the EM wave absorber with the composition ratio in Amorphous : CPE = 60 : 40 wt.% with the thickness of 4 mm has the absorption ability more than 35 dB at 2.4 GHz. Thus, it is expected the wireless LAN environment can be improved by using the developed absorber.

Generally, a silicone rubber and a chlorinated polyethylene(CPE) have been used as a binder for the development of high-performance composite EM(Electro Magnetic) wave absorbers. In this paper, the EM wave absorption performance of natural lacquer, which is newly proposed as a binder was investigated. The prepared MnZn ferrite EM wave absorbers are mixed with natural lacquer showed excellent EM wave absorption characteristics compared with MnZn ferrite EM wave absorbers which are mixed with the conventional binders. MnZn ferrite EM wave absorbers mixed with natural lacquer were prepared and their absorption ability was also investigated The EM wave absorbers are fabricated in different proportions of MnZn, or NiZn ferrite and natural lacquer, and their reflection coefficients are measured. The permittivity and permeability are calculated by using the measured reflection coefficients. The EM wave absorption abilities are calculated according to different thicknesses of the EM wave absorbers.

In this paper, the EM wave absorbers were designed and fabricated for X -band sensors using Carbon of dielectric material with CPE. The complex relative permittivity of samples is calculated by using measurement results of S-parameter. We simulated the double-layered type EM wave absorber with broad bandwidth using the measured complex relative permittivity by changing the thickness and layer, which was fabricated based on the simulated design The fabricated EM wave absorber consists of 1 mm first layer sheet facing metal with Carbon composition ratio 70 vol. % and 1.5 mm second layer sheet with Carbon composition ratio 60 vol. %. The measured results showed a good agreement to the simulated ones. It is found toot the optimized absorption ability of double-layered type EM wave absorber with thickness of 2.5 mm is higher than 10 dB from 7.8 GHz to 13.3 GHz.