To prepare weather-resistant modified silane acrylic resin coatings for an architectural purpose, tetrapolymers were synthesized by radical polymerization. 3-Methacryloxypropyltrimethoxysilane (MPTS) as a silicone monomer and n-butyl acrylate, methyl methacrylate, and n-butyl methacrylate as acrylic monomers were used. The composition of monomers was adjusted to fix the glass transition temperature of acrylic polymer for 20℃. The composition of MPTS in the synthesized polymer were varied from 10 wt% to 30 wt%. On the basis of synthesized resin amber paints were prepared and their physical properties and effects on weatherability were examined. The presence of MPTS in modified silane acrylic resins generally resulted in low molecular weight and broad molecular weight distribution, and also lowered the viscosity of the copolymers. The coated films prepared from these resins showed good and balanced properties in general. Adhesion to the substrate was outstanding in particular. Weatherability tests were carried out in three different types such as outdoor exposure, QUV, and SWO. The test results showed that the modified silane acrylic resins containing 30 wt% of MPTS had superior weathering properties.

Chlorine-containing modified polyester polyols were synthesized by two-step condensation reactions. Intermediate was synthesized by the esterification of monochloroacetic acid with trimethylolpropane in the first step. Polycondensation of the intermediate (MCAOs), 1,4-butanediol, and trimethylolpropane with adipic acid was carried out. Two-component polyurethane (PU) coatings were prepared by blending MCAOs and IPDI-isocyanurate. There new flame-retardant coatings showed various properties comparable to other non-flame-retardant coatings. They were superior to flammable coatings from the experimental results showing rapid and 10 to 13 hours of pot-life. Coatings with 30wt% monochloroacetic acid was not flammable by the vertical flame retardancy test.

New electroluminescent materials based on anthracene chromophore with naphthylethenyl substituent, 9,10-bis(α-naphthylethenyl)anthracene (a-BNA), as well as four kinds of its derivatives were synthesized, and luminescent properties of these materials were investigated. Electrolumineecent(EL) emission band was discussed based on their substituent structure differences. It was found that the emission band strongly depends on the molecular structure of introduced substituent. It can be tuned from 557 nm to 591 nm by changing the substituent structures. On the other hand, the anthracene chromophore with bulky substituent possessed high melting point and they gave stable films through vacuum-sublimation. The double layer EL device of ITO/TPD/emission layer/Mg:Ag was employed, and exhibited efficient orange light originating from emitting materials. EL emission with a maximum luminance was observed in the b-BNA emitting material, : maximum luminance was about 8,060 cd m-2 at an applied voltage of 10 V and current density of 680 mA/cm2. In conclusion, the electroluminescent properties also showed good difference with their substituent structure.