Three point bending tests of single edge notched beam (SENB) specimens were carried out to evaluate the fracture behavior of the fine-grain isotropic nuclear grade graphite, IG-11. To measure the crack initiation point and the subsequent crack growth, the direct current potential drop (DCPD) method and a traveling microscope were used. The effects of test variables like initial crack length, specimen thickness, notch type and loading rate on the measured fracture toughness, KQ, were investigated. Based on the test results, the ranges of the test variables to measure the reliable fracture toughness value were proposed. During the crack growth, the rising R-curve behavior was observed in IG-11 graphite when the superficial crack length measured on the specimen surface was used. The increase of crack growth resistance was discussed in terms of crack bridging, crack meandering, crack branching, microcracking and crack deflection, which increase the surface energy and friction force.

발전소 내 방사화 부식생성물의 대부분을 차지하고 있는 니켈 페라이트계 부식생성물을 모사 발생시키기 위한 고온 고압용 장치를 제작하여 연구를 수행하였다. 배관형 포집기를 이용한 부식생성물 발생장치로부터 방사화 부식생성물과 가장 유사한 부식생성물을 얻을 수 있었다. 발전소에서 입자성 부식생성물이 발생되는 원리인 온도에 따른 용해도 차이를 구현하기 위하여 270C에서 부식반응이 일어나 상대적으로 높은 온도를 가진 포집용 장치에 부식생성물이 포집되도록 장치를 제작하였으며 , 발생된 부식생성물은 주사전자현미경 관찰과 EDAX를 통한 조성분석으로 그 특성을 관찰하였다. 부식생성물은 포집 된 위치 에 따라서 침상 형태의 산화물과 결정 형태의 산화물로 나뉘었으며, 조성 분석 결과 결정 형태의 부식생성물이 니켈 페라이트로서 발전소에서 발생되는 입자성 부식생성물과 유사한 것을 알 수 있었다.