Here, we report the preparation of microporous-activated carbons from a Brazilian natural lignocellulosic agricultural waste, cupuassu shell, by pyrolysis at 500 ºC and KOH activation under different experimental conditions and their subsequent application as adsorbent for CO2 capture. The effect of the KOH:precursor ratio (wt/wt%) and the activation temperature on the porous texture of activated carbons have been studied. The values of specific surface area ranged from 1132 to 2486 m2/ g, and the overall micropore volume ranged from 0.73 to 1.02 cm3/ g. Carbons activated with 2:1 ratio of KOH and activation temperature of 700 ºC presented a CO2 adsorption at 1 bar of 7.8 and 4.4 mmol/g at 0 °C and 25 ºC, respectively. The isosteric heat of adsorption, Qst , was calculated for all samples by applying the Clausius–Clapeyron approach to CO2 adsorption isotherms at both temperatures. The values of CO2 adsorption capacities are among the highest reported in the literature, especially for activated carbons produced from biomass.

The possibility of orange pulp utilization for nanoporous carbons production was investigated. Moreover, processing the obtained materials as limonene oxidation catalysts was studied as well. Limonene was separated from orange pulp obtained from fragmented orange peels—the waste from industrial fruits processing—by means of simple distillation. After the separation of limonene from the biomass, the dried orange pulp was converted to three types of nanoporous carbon catalysts: without activating agent, with NaOH, and with KOH. The catalysts were characterized by XRD, SEM, EDX, AFM, and sorption of N2 methods. The activities of the obtained catalysts were tested in the oxidation of limonene to perillyl alcohol (the main product), carveol, carvone, and 1,2-epoxylimonene and its diol. In the oxidation processes, hydrogen peroxide was used as the oxidizing agent. This work has shown for the first time that nanoporous carbons obtained from orange pulp waste, after separation of limonene, are active catalysts for limonene oxidation to industrially important value-added products.