The thermocatalytic decomposition of methane is a promising method for hydrogen production. To determine the cause of carbonaceous catalyst deactivation and to produce high-value carbon, methane decomposition behavior and deactivated catalysts were analyzed. The surface properties and crystallinity of a commercial activated carbon material, MSP20, used as a methane decomposition catalyst, varied with the reaction time at a reaction temperature of 900 °C. During the initial reaction, MSP20 provided a methane conversion of ≥ 50%; however, the catalyst exhibited rapid deactivation as crystalline carbon grew at surface defects; after 15 min of reaction, approximately 33% methane conversion was maintained. With increasing reaction time, the specific surface area of the catalyst decreased, whereas crystallinity increased. The R-square value of the conversion–crystallinity relationship was significantly higher than that of the conversion–specific surface area relationship; however, neither profile was linear. The activity of the activated carbon catalyst for methane decomposition is mainly determined by the complex actions of the specific surface area and defect sites. The activity was maintained after an initial sharp decline caused by the continuous growth of crystalline carbon product. This study presents the application of carbonaceous catalysts for the decomposition reaction of methane to form COx- free hydrogen, while simultaneously yielding porous carbon materials with an improved electrical conductivity.

This paper proposes the optimal molecular weight for a petroleum-based binder pitch to enhance the density and strength of the prepared graphite block. The effect of the molecular weight on the binder properties, which was quantified using solvent fractionation, was considered based on the evaluation of the coking and viscosity characteristics. The affinity of the pitch to coke influenced the carbonization yield of the block, and the proportion of closed pores was reduced via the use of a highaffinity binder pitch. In addition, the viscosity was found to influence the uniformity of the coke and pitch dispersions, and numerous open pores were formed in the graphite block under high-viscosity conditions. In terms of the molecular weight, a reduction in the content of the insoluble 1-methyl-2-pyrrolidone (NMP) fraction, which was the heaviest fraction present in the pitch, was found to reduce the affinity of the binder to coke while increasing its viscosity. Therefore, the density and strength of the prepared graphite block were reduced upon increasing the insoluble NMP content of the binder pitch. Consequently, it was necessary to control the content of this fraction within < 13.81 wt% to obtain high-density and high-strength graphite blocks.

Large earthquakes with (MW > ~ 6) result in ground shaking, surface ruptures, and permanent deformation with displacement. The earthquakes would damage important facilities and infrastructure such as large industrial establishments, nuclear power plants, and waste disposal sites. In particular, earthquake ruptures associated with large earthquakes can affect geological and engineered barriers such as deep geological repositories that are used for storing hazardous radioactive wastes. Earthquake-driven faults and surface ruptures exhibit various fault zone structural characteristics such as direction of earthquake propagation and rupture and asymmetric displacement patterns. Therefore, estimating the respect distances and hazardous areas has been challenging. We propose that considering multiple parameters, such as fault types, distribution, scale, activity, linkage patterns, damage zones, and respect distances, enable accurate identification of the sites for deep geological repositories and important facilities. This information would enable earthquake hazard assessment and lower earthquakeresulted hazards in potential earthquake-prone areas.

This study examined the effects of micro- (crystallinity) and macro (orientation)-crystalline properties of graphite on the initial efficiency, discharge capacity, and rate performance of anodic materials. Needle coke and regular coke were selected as raw materials and pulverized to 2–25 μm to determine the effects of crystalline properties on particle shape after pulverization. Needle coke with outstanding crystallinity had high initial efficiency, and smaller particles with larger specific surface areas saw increased irreversible capacity due to the formation of SEI layers. Because of cavities existing between crystals, the poorer the crystalline properties were, the greater the capacity of the lithium ions increased. As such, regular coke had a 30 mAh/g higher discharge capacity than that of needle coke. Rate performance was more affected by particle size than by crystalline structure, and was the highest at a particle distribution of 10–15 μm.

Celecoxib, a cyclooxygenase (COX)-2 selective inhibitor, was approved as a non-steroidal anti-inflammatory drug (NSAID), and this therapeutic application has been expanded to several other diseases, including colon cancer. Notably, a treatment strategy combining the use of celecoxib and radiation therapy has been employed for improving the control of local cancers. In this study, we examined the effect of celecoxib on irradiation-induced intestinal damage. The twenty four mice (BALB/c) were divided into four groups; 1) sham-irradiated control group, 2) celecoxib-treated group, 3) irradiated group, and 4) celecoxib-treated irradiation group. Mice were orally administered celecoxib at a dose of 25 mg/kg in a 0.1 mL volume, daily for 4 days after irradiation exposure (10 Gy). Then, histological examinations of the jejunal villous height, crypt survival, and crypt size were performed. The expression of COX-2 after administration of celecoxib in irradiated mice was examined by employing immunohistochemistry, Western blotting, and qPCR analysis. The jejunal villi height and the crypt survival were reduced in the irradiation group compared with the sham-irradiated group. Celecoxib treatment in irradiation mice even more decreased those indicators. Crypt size was increased in the radiation group compared to the sham-irradiated control group, whereas the size was decreased in the celecoxibtreated irradiation group compared with the group exposed to the radiation injury. COX-2 expression was detected in the crypt of the small intestine, and COX-2 expression was increased in the crypt lesion following radiation exposure. However, COX-2 expression was reduced in the celecoxib-treated irradiation group. Therefore, in the present study, we confirmed that celecoxib treatment after irradiation aggravated the irradiation-induced intestinal damage. These results suggest that a caution need to be administered when celecoxib treatment is performed in combination with radiation therapy for cancer treatment.

Continuous synthesis of high-crystalline carbon nanotubes (CNTs) is achieved by reconfiguring the injection part in the reactor that is used in the floating catalyst chemical vapor deposition (FC-CVD) process. The degree of gas mixing is divided into three cases by adjusting the configuration of the injection part: Case 1: most-delayed gas mixing (reference experiment), Case 2: earlier gas mixing than Case 1, Case 3: earliest gas mixing. The optimal synthesis condition is obtained using design of experiment (DOE) in the design of Case 1, and then is applied to the other cases to compare the synthesis results. In all cases, the experiments are performed by varying the timing of gas mixing while keeping the synthesis conditions constant. Production rate (Case 1: 0.63 mg/min, Case 2: 0.68 mg/min, Case 3: 1.29 mg/min) and carbon content (Case 1: 39.6 wt%, Case 2: 57.1 wt%, Case 3: 71.6 wt%) increase as the gas-mixing level increases. The amount of by-products decreases stepwise as the gas-mixing level increases. The IG/ID ratio increases by a factor of 7 from 10.3 (Case 1) to 71.7 (Case 3) as the gas-mixing level increases; a high ratio indicates high-crystalline CNTs. The radial breathing mode (RBM) peak of Raman spectrograph is the narrowest and sharpest in Case 3; this result suggests that the diameter of the synthesized CNTs is the most uniform in Case 3. This study demonstrates the importance of configuration of the injection part of the reactor for CNT synthesis using FC-CVD.

The carbon anode material for lithium-ion battery was prepared by pyrolysis fuel oil and waste polyethylene terephthalate (PET) additive. The pitch was synthesized as a medium material for carbon anode by heat treatment. The waste PET additive improved the softening point and thermal stability of the pitch. La and Lc of the anode material (heat-treated pitch) increased at higher treatment temperature but decreased by waste PET additive. The electric capacity was evaluated based on effects of defective cavity and developed graphite interlayer, respectively. When the La and Lc of the anode material decreased, the electric capacity by cavity increased based on defective graphite structure. Therefore, the addition of waste PET causes the improved capacity by the cavity. The anode material which has a high efficiency (over 95%) and C-rate (95%, 2 C/0.1 C) was obtained by controlling the process of heat treatment and PET addition. The mechanism of lithium-ion insertion was discussed based on effects of defective cavity and developed graphite interlayer.

In this study, pitch crosslinked by oxygen function groups was made into activated carbon (AC) and pore structure was observed. The oxygen functional groups were introduced by the addition of waste PET for pitch synthesis. Activation agent ratios used to obtain the AC during the activation process were 1:1, 1:2 and 1:4 (pitch:KOH, w/w). The oxygen content in the prepared pitch was characterized by elemental analysis. Also, the molecular weight of pitch was investigated by MALDITOF. Specific surface area and micropore volume of the prepared AC were determined by the argon adsorption–desorption analysis and calculated using the Brunauer–Emmett–Teller and Horvath–Kawazoe equations, respectively. Micropore fraction of PET-free AC was smaller than that of PET-added AC. At high activation agent ratio, mesopores were created when the micropore structure collapsed. However, in the PET-added AC, due to the oxygen crosslinking effect, the micropore structure and micropore size were maintained even at a high activation agent ratio. Therefore, PET AC was found to have a higher micropore fraction than that of PET-free AC.

The mesophase pith was synthesized based on effects of a high-pressure thermal condensation and feed (PFO/FCC-DO) blending. The reaction conditions were designed by fluidity and reactivity of each feed during the thermal reaction. The high-pressure thermal condensation process disturbs distillation of the volatile compounds in pyrolysis fuel oil (PFO); the fluidity can be controlled. In the blending process, PFO, which has a high thermal condensation reactivity, and fluid catalytic cracking-decant oil (FCC-DO), which maintains fluidity, interacted with a synergistic effect. Thus, mesophase pitch with a large mesophase content was manufactured by the two above processes.

Coke aggregates and carbon artifacts were produced to investigate the interactions of coke and pitch during the kneading process. In addition, the kneading ratio of the coke and binder pitch for the coke aggregates was controlled to identify the formation of voids and pores during carbonization at 900°C. Experiments and thermogravimetric analysis revealed that carbon yields were improved over the theoretical yield calculated by the weight loss of the coke and binder pitch; the improvement was due to the binding interactions between the coke particles and binder pitch by the kneading process. The true, apparent, and bulk densities fluctuated according to the kneading ratio. This study confirmed that an excessive or insufficient kneading ratio decreases the density with degradation of the packing characteristics. The porosity analysis indicated that formation of voids and pores by the binder pitch increased the porosity after carbonization. Image analysis confirmed that the kneading ratio affected the formation of the coke domains and the voids and pores, which revealed the relations among the carbon yields, density, and porosity.

소나무재선충병의 나무주사는 살선충제를 중심으로 실시되어 왔으며, 매개충인 솔수염하늘소와 북방수염하늘소의 방제는 주로 항공방제나 지상방제를 통하여 이루어졌다. 본 연구에서는 나무주사를 통하여 매개충 (솔수염하늘소)을 방제하기 위한 연구로 Abamectin+Acetamiprid ME, Thiamethoxam DC 약제의 나무주사시 솔수염하늘소의 약효발현농도, 처리 후 기간별 효과(2017년~2018년)를 검토하였다. 실내 발현농도 시험에서는 Acetamiprid, Thiamethoxam LC50 value는 각각 0.102ppm, 0.083ppm 으로 나타 났으며, 야산(포장)에서 Abamectin+Acetamiprid ME, Thiamethoxam DC 처리구의 100.0% 치사 소요일 수는 처리 90일 후 11.0일, 9.4일, 처리 360일 후 11.6일, 10.0일로 나타나서 두 약제 모두 3월 처리시 다음해에 발생하는 매개충 (솔수염하늘소) 방제까지 가능함을 확인 할 수 있었다.

The Semi-Rigid Pavement (SRP) mixture is composed of Gap Graded Asphalt (GGA) mixture (air void = 20~28%) and cement paste. By inserting cement paste into voids in GGA mixture, SRP can provide not only flexibility but also rigidity characteristics on pavement performance. SRP can mitigate pavement surface temperature increase during summer session, provide better smoothness and mitigate rutting distress due to heavy weight vehicles, successfully. In Japan, SRP is widely applied in cross section area, heavy vehicle parking lot and highway ticketing booth in highway network system. In South Korea, SRP was introduced and applied since 2005. However, still more researches and studies are needed to understand material characteristics and improve performance of SRP. Moreover, the current SRP system in South Korea merely follows and adapts the aggregate gradation information from Japan which needs to be amended and customized into original material (i.e. aggregate, binder and cement) situation of South Korea. In this paper, SRP system based on Stone Mastic Asphalt (SMA) mixture design originated from Korea Expressway Corporation (KEC) and enhanced cement paste with addition of fly-ash and slags was developed. In addition, an optimized proportion between asphalt mixture air voids and cement paste amount with consideration of economic benefit was introduced. Based on field evaluation process it can be said that the newly developed SRP system can successfully adapted not only in static site on highway: parking lots or ticketing booth, but also in dynamic site on highway: driving and wheel path.

In case of performing asphalt pavement overlay on existing concrete pavement layer, applying asphalt emulsion tack-coating or spreading prime-coating is considered to improve adhesion between asphalt and concrete layer. After coating work is done a curing process is considered not only for promoting evaporation process in coated (and/or spread) asphalt emulsion, but also for generating a membrane which can act as a bonding agent. Finally, asphalt overlay construction is performed when this curing process is completely done. However, during asphalt overlay construction process remarkable amount of spread tack-coating layer is lost due to asphalt material transfer vehicles (e.g. trucks, approximately 40~50% of total spread tack coating material is lost). In this paper, a new pavement equipment contains simultaneous asphalt emulsion spreading ability and corresponding construction techniques are introduced. Through applying this equipment, non-stop two step sequent working process: spreading asphalt emulsion on to existing concrete pavement layer then paving asphalt material for overlay construction, is available. During pavement working process temperature of asphalt material was kept with ranged between 130ºC and 170ºC. After performing field performance evaluation, it was found that crucial improvement in pavement layer adhesion, crack and rutting resistant ability were observed compared to the conventional paving method.

Pyrolyzed fuel oil (PFO) and coal tar was blended in the feedstock to produce pitch via thermal reaction. The blended feedstock and produced pitch were characterized to investigate the effect of the blending ratio. In the feedstock analysis, coal tar exhibited a distinct distribution in its boiling point related to the number of aromatic rings and showed higher Conradson carbon residue and aromaticity values of 26.6% and 0.67%, respectively, compared with PFO. The pitch yield changed with the blending ratio, while the softening point of the produced pitch was determined by the PFO ratio in the blends. On the other hand, the carbon yield increased with increasing coal tar ratio in the blends. This phenomenon indicated that the formation of aliphatic bridges in PFO may occur during the thermal reaction, resulting in an increased softening point. In addition, it was confirmed that the molecular weight distribution of the produced pitch was associated with the predominant feedstock in the blend.

This research considers the effect of added mesophase pitch (MP) as an additive during the pitch synthesis reaction of pyrolyzed fuel oil (PFO). Two effects are generated by adding MP. One is an enhancement of thermal stability due to the high thermal property of the additive; the other is that the volatile compounds that were removed by vaporization of PFO during the thermal reaction can participate in the pitch synthesis reaction (PFO→pitch) more efficiently. The effect differs according to the amount of the additive. When the amount of the additive is less than 7 wt%, the first effect is dominant, whereas the second effect is dominant when the additive amount exceeds 10 wt%.

Previous studies indicated that Matsumuraeses phaseoli and M. falcana (Lepidoptera: Tortricidae) are separate species since a few differences were observed in genitalia morphology and female sex pheromone composition. A clear difference was detected in the DNA sequences of cytochrome oxidase I of the two species separately collected in different plants and regions. A hybridization test also showed that a post-zygotic reproductive isolation occurred between the species. In field monitoring, however, both species have been caught simultaneously and together in the separate sex pheromone traps installed for the two species around neighboring soybean and red bean fields. Molecular marker-assisted identification with several adults sampled from the trapped insects showed that only ca. 40% of M. phaseoli adults identified as the species by genitalia morphology was the M. phaseoli, while ca. 97% of M. falcana adults identified as the species was the M. falcana. The result indicated that the observation of genitalia did not make a decisive criterion for classification of the insects. Conclusively, it suggested that the sex pheromones of the two species should be studied more precisely although there is a possibility that the two species are hybridized in fields as in laboratory, and speciation is under process.

Cholesterol granuloma(CG) occurs frequently in association with chronic middle ear diseases, particularly diseases in the mastoid antrum and air cells of the temporal bone, and much less frequently in paranasal sinuses. It occurs frequently secondary to massive hemorrhage of oral and paraoral cysts. However, It has never been reported to occur solely without any association with preexisting lesion in the mandible. We experienced development of unusual cholesterol granuloma in the mandible. Seventy year old female presented diffuse hard swelling on the left mandibular area with lymphadenopathy of the left cervical lymph node. Radiographic examination showed a well circumscribed multilocular radiolucency resembling soap bubble appearance with tooth displacement and root resorption, leading to the radiogrphic impression of dentigerous cyst or odontogenic cyst or ameloblastoma. CT showed bucco-lingually undulating expansile lesion with corticated margin from the left posterior mandibular body to the anterior ramus, including #46, #47 and #48, and the mass showed slightly lower attenuation than muscle. leading to the impression of ameloblastoma. The mass after surgical excision composed of 2 sac like structures, measuring 4.0cm, and 2.7cm in diameter respectively. One sac was tightly attached to the #46, resembling dentigerous cyst. Microscopic examination showed a large number of cholesterol clefts in association with hemorrhage, hemosiderin pigments and foreign body giant cells. There was no evidence of cyst or other lesions

Cloned calves derived from somatic cell nuclear transfer (SCNT) have been frequently lost by sudden death at 1 to 3 month following healthy birth. To address whether placental anomalies are responsible for the sudden death of cloned calves, we compared protein patterns of 2 placentae derived from SCNT of Korean Native calves died suddenly at two months after birth and those of 2 normal placentae obtained from AI fetuses. Placental proteins were separated using 2-Dimensional gel electrophoresis. Approximately 800 spots were detected in placental 2-D gel stained with coomassie-blue. Then, image analysis of Malanie III (Swiss Institute for Bioinformatics) was performed to detect variations in protein spots between normal and SCNT placentae. In the comparison of normal and SCNT samples, 8 spots were identified to be up-regulated proteins and 24 spots to be down-regulated proteins in SCNT placentae, among which proteins were high mobility group protein HMG1, apolipoprotein A-1 precursor, bactenecin 1, tropomyosin beta chain, H+-transporting ATPase, carbonic anhydrase II, peroxiredoxin 2, tyrosine-rich acidic matrix protein, serum albumin precursor and cathepsin D. These results suggested that the sudden death of cloned calves might be related to abnormal protein expression in placenta.