Maca has been reported to alleviate male menopause symptoms in humans and experimental animals; however, its mechanism of action in improving male menopause has not been clearly identified. This study aimed to investigate the mechanism of action of gelatinized maca in improving male menopause by analyzing serum testosterone, testicular androgen receptor (AR) expression, and testicular oxidation-antioxidation balance. Gelatinized maca was administered orally to aged male C57BL/6 mice at three doses (500, 1,000, and 1,500 mg/kg/day) for 28 consecutive days. Serum biochemical analysis showed an increase in serum hydroxysteroid 17-beta-dehydrogenase 13 (HSD17β13) concentration at 1,500 mg/kg/day and a decrease in serum sex hormone-binding globulin (SHBG) concentration at ≥ 1,000 mg/kg/day. Gelatinized maca administration also resulted in the increased expression levels of testicular AR and cyclic adenosine monophosphate (cAMP) response element binding protein (CREB) at 1,500 mg/kg/day. Oxidative stress analysis showed an increase in testicular superoxide dismutase and glutathione reductase activities and a decrease in testicular malondialdehyde at 1,500 mg/kg/day. In conclusion, gelatinized maca administration to aged male mice increased HSD17β13, AR and CREB expression, and antioxidant capacity and decreased serum SHBG. The results of the present study suggest that gelatinized maca may be a useful substance that can help alleviate male menopause symptoms.
This study explored the possibility of forming a coating layer containing alginic acid on the surface of a magnesium alloy to be used as a biomaterial. We formed a coating layer on the surface of a magnesium alloy using a plasma electrolytic oxidation process in an electrolytic solution with different amounts of alginic acid (0 g/L ~ 8 g/L). The surface morphology of all samples was observed, and craters and nodules typical of the PEO process were formed. The cross-sectional shape of the samples confirmed that the thickness of the coating layer became thicker as the alginic acid concentration increased. It was confirmed that the thickness and hardness of the sample significantly increase with increasing alginic acid concentration. The porosity of the surface and cross section tended to decrease as the alginic acid concentration increased. The XRD patterns of all samples revealed the formation of MgO, Mg2SiO4, and MgF2 complex phases. Polarization tests were conducted in a Stimulate Body Fluid solution similar to the body's plasma. We found that a high amount of alginic acid concentration in the electrolyte improved the degree of corrosion resistance of the coating layer.