A series of high capacity soft carbons with different phosphorus contents were successfully prepared by carbonizing petroleum cokes treated with hypophosphorous acid at 900˚C. The effect of phosphorus content on the electrochemical performance of the soft carbons was extensively investigated. The P-doped soft carbons exhibited greatly enhanced discharge capacities and outstanding rate capabilities with increasing phosphorus content. In addition, the influence of temperature on the electrochemical behaviors of the soft carbons was investigated in a wide temperature range of 25˚C to 50˚C. Surprisingly, the electrochemical properties of the pristine and P-doped soft carbons were highly sensitive to the operating temperature, unlike conventional graphite. The pristine and P-doped soft carbons exhibited significantly high discharge capacities of 470 and 522 mAh/g, respectively, at a high temperature of 50˚C.

물/Span 80-Tween 80/긴 사슬 파라핀 오일 계에서 PIC (조성 상전이) 방법을 이용하여 O/W 나노에멀젼을 제조하였다. 제조 온도를 30 ℃에서 80 ℃로 상승시킴에 따라 제조된 나노에멀젼의 입경은 120 nm에서 40 nm로 감소하여 나노에멀젼을 형성하였다. 혼합 계면활성제의 HLB를 변화시킴에 따라 12.0 ~ 13.0 부근에서 가장 작은 입경을 형성하는 최적 HLB가 존재하였다. 나노에멀젼의 점도는 액적의 부피 분율(ϕ)에 따라 현격하게 증가하였으나, 입경의 크기는 약간 증가하였다. 그리고, ϕ ≤ 0.3 조건에서 나노에멀젼의 크기 분포는 2 개월 이상 일정하게 유지 되었다. 이러한 결과는 점성 파라핀 오일의 경우 30 ℃에서는 PIC 방식으로 거의 분산 할 수 없음을 보여주지만, 제조 온도가 증가할 경우 단 분산 나노에멀젼의 제조가 가능하다는 것을 보여준다. 나노에멀젼이 생성되면, Ostwald ripening에 대한 안정성은 연속 상에서 액상 파라핀 오일의 매우 낮은 용해도로 인해 안정하게 되며, 이는 화장품 응용에서 매우 중요하다.