Graphite crystals consist of a layered structure with stacked graphene sheets, and exhibit self-lubricating properties due to the facile sliding of graphene layers in the horizontal direction, facilitated by weak Van der Waals bonds along the c-axis. When this graphite material is impregnated with a lubricating liquid, it forms a solid and stable lubricating layer, and effectively reduces damage to the counter material from friction-induced wear under conditions of high-load reciprocating motion. This study investigates how oxidation-induced pore expansion and the silane treatment of graphite affect lubricating oil impregnation behavior, the friction coefficient of impregnated graphite, frictional stability, and microstructural changes at the friction surface. It was found that graphite oxidation within the chemical reaction temperature range enhanced porosity and increased the rate of lubricating oil impregnation. The functionalization of the graphite surface with hydrophobic silane coupling agents also significantly enhanced oil uptake, with a pronounced observed improvement when utilizing hydrophobic oils. Under a vertical load of 360 kgf and a surface pressure of 3 MPa, the graphite surface treated with hydrophobic silane and impregnated with oil exhibited the lowest average friction coefficient of 0.192 over 600 cycles. During the friction and wear process, a lubricating layer formed on the graphite surface, which contributes to stable wear performance. This surface modification strategy offers high applicability in industries such as automotive, aerospace, and heavy machinery, with the potential to significantly enhance component performance and extend service life under high-load, low-speed reciprocating conditions.

In this work, we investigated the photo-degradation performance of MnO2-SiC fiber-TiO2 (MnO2-SiC-TiO2) ternary nanocomposite according to visible light excitation utilizing methylene blue (MB) and methyl orange (MO) as standard dyes. The photocatalytic physicochemical characteristics of this ternary nanocomposite were described by X-ray diffraction (XRD), scanning electron microscopy (SEM), tunneling electron microscopy (TEM), ultraviolet-visible (UV-vis), diffuse reflectance spectroscopy (DRS), electrochemical impedance spectroscopy (EIS), photocurrent and cyclic voltammogram (CV) test. Photolysis studies of the synthesized MnO2-SiC-TiO2 composite were conducted using standard dyes of MB and MO under UV light irradiation. The experiments revealed that the MnO2-SiC-TiO2 exhibits the greatest photocatalytic dye degradation performance of around 20 % with MB, and of around 10 % with MO, respectively, within 120 min. Furthermore, MnO2-SiC-TiO2 showed good stability against photocatalytic degradation. The photocatalytic efficiency of the nanocomposite was indicated by the adequate photocatalytic reaction process. These research results show the practical application potential of SiC fibers and the performance of a photocatalyst composite that combines these fibers with metal oxides.