To enhance mechanical properties through improvement of dispersion stability of carbon black (CB) in epoxy resins, fluorine functional groups were introduced on the CB surface by fluorination. The changes in the chemical properties and dispersion stabilities after fluorination were evaluated with different partial pressures of fluorine gas. The mechanical properties of the fluorinated CB/epoxy composites were evaluated by the test of tensile, impact strengths and creep behavior. The fluorinated CB/epoxy composites showed approximately 1.6 and 1.1 times enhancement in the tensile and impact strengths compared to that of neat epoxy, respectively. Moreover, when a constant load was applied at 323 K, the fluorinated CB/epoxy composites lasted longer and had smaller strain changes than those of the raw CB/epoxy composites. Thus, well-dispersed CB by fluorination in epoxy resins effectively transfers mechanical stress.

To enhance the thermal properties of epoxy composites, expanded graphite (EG) was oxyfluorinated and embedded into epoxy resin as a reinforcement. The maximum thermal conductivity was obtained for epoxy composites with oxyfluorinated EG, representing a 62% increase compared to that of neat epoxy. Additionally, the glass transition temperature (Tg) and integral procedural decomposition temperature of epoxy composites with oxyfluorinated EG show the increase of 6% (4.4 °C) and 106% (264 °C), respectively, which indicated the improvement in thermal stability. These results can be attributed to the interfacial interaction between epoxy and oxyfluorinated EG, which formed strong interfacial interactions between the epoxy resin and EG due to the presence of oxygen- and fluorine-containing functional groups in oxyfluorinated EG.