In this work, the effect of catalysts on the mechanical properties of carbon fibers-reinforced epoxy matrix composites cured by cationic latent thermal catalysts, i.e., N-benzylpyrazinium hexafluoroantimonate (BPH) was studied. Differential scanning calorimetry was executed for thermal characterization of the epoxy matrix system. Mechanical interfacial properties of the composites were studied by interlaminar shear strength (ILSS), critical stress intensity factor (KIC), and specific fracture energy (GIC). As a result, the conversion of neat epoxy matrix cured by BPH was higher than that of one cured by diaminodiphenyl methane (DDM). The ILSS, KIC, GIC, and impact strength of the composites cured by BPH were also superior to those of the composites cured by DDM. This was probably the consequence of the effect of the substituted benzene group of BPH catalyst, resulting in an increase in the cross-link density and structural stability of the composites studied.

This study aimed to investigate the influence of mesoporous carbons on the thermal insulation properties of epoxy/mesoporous carbon composites. The mesoporous carbon (CMK-3) was prepared by conventional templating method using SBA-15. The epoxy/mesoporous carbon composites were prepared by mixing the synthesized CMK-3 with diglycidylether of bisphenol A (DGEBA). As experimental results, the curing reactivities of the DGEBA/CMK-3 composites were found to decrease with the addition of the CMK-3. Also, the thermal conductivities of DGEBA/CMK-3 composites were found to decrease with increasing CMK-3 content. This could be interpreted in terms of the slow thermal diffusion rate resulting in pore volume existing in the gaps in the interfaces between the mesoporous carbon and the DGEBA matrix.

In this work, the effect of co-carbon fillers on the electrical and mechanical properties of epoxy nanocomposites was investigated. The graphite nanosheets (GNs) and multi-walled carbon nanotubes (MWNTs) were used as co-carbon fillers. The results showed that the electrical conductivity of the epoxy nanocomposites showed a considerable increase upon an addition of MWNTs when GNs were fixed at 2 wt.%. This indicated that low content GNs formed the bulk conductive network and then MWNTs added were intercalated between the GN layers, resulted in the formation of additional conductive pathway. Furthermore, the flexural strength of the epoxy nanocomposites was enhanced with increasing the MWNT content. It was probably attributed to the flexible MWNTs compared with rigid GNs, resulted in the enhancement of the mechanical properties.

In this work, the effect of carbon nanofibers (CNFs) addition on physicochemical characteristics of CNFs-reinforced epoxy matrix nanocomposites was studied. Poly(amide imide) solutions in dimethylformamide were electrospun into webs consisting of 250±50 nm fibers which were used to produce CNFs through stabilization and carbonization processes. As a result, the CNFs with average diameter of 200±20 nm were obtained after carbonization process. The nanocomposites with CNFs showed an improvement of thermal stability parameters and fracture toughness factors, compared to those of the specimen without CNFs, which could be probably attributed to the higher specific surface area and larger aspect ratio of CNFs, resulting in improving the mechanical interlocking in the nanocomposites. Also, the applied external loading can effectively transfer to CNFs because strong interactions are resulted between the epoxy matrix and the CNFs.

Carbon fibers are a new breed of high-strength materials which have been described as a fiber containing at least 90% carbon obtained by the controlled pyrolysis of appropriate fibers. Carbon fiber composites are ideally suited to applications where strength, stiffness, lower weight, and outstanding fatigue characteristics are critical requirements. They also can be used in the occasion where high temperature, chemical inertness and high damping are important. In recent decades, carbon fibers have found wide applications in commercial and civilian aircraft, recreational, industrial, and transportation markets. Therefore, understanding the basic structure, synthesis and physicochemical properties of carbon fibers is very important to apply them as a precursor of above applications. This review paper discuss the general information and manufacture technique of carbon fibers used for improving the performance of composite materials in various industries for the present.