Epoxy resin (EP) is a thermosetting resin with excellent properties, but its application is limited due to its high brittleness and poor flame retardancy. Therefore, to solve this problem, a dispersion system of imidazole-containing ionic liquid ([Dmim]Es) and graphene in epoxy resin is designed based on the π–π stacking effect between imidazole and graphite layers. The study on the thermal and flame-retardant properties of the composites show that the modified [Dmim]Es–graphene nanosheets improved the flame retardancy, smoke suppression and thermal stability of epoxy resin. With the addition of 5wt% [Dmim]Es and 1% Gra, the exothermic rate (HRR) and total exothermic (THR) of the composites decrease by 35% and 30.2% compared with the untreated epoxy cross-linking, respectively. The limiting oxygen index reaches 33.4%, the UL-94 test rating reaches V-0. The characterization of mechanical properties shows that the tensile properties and impact properties increased by 13% and 30%, respectively. Through SEM observation, the addition of [Dmim]Es improves the dispersion of graphene in the EP collective and changes the mechanical fracture behavior. The results show that ionic liquid [Dmim]Es-modified graphene nanosheets are well dispersed in the matrix, which not only improves the mechanical properties of epoxy resin (EP), but also has a synergistic effect on flame retardancy. This work provides novel flame-retardant and graphene dispersion methods that broaden the range of applications of epoxy resins.

The evolvement in the microstructure and electrical properties of PAN-based carbon fibers during high-temperature carbonization were investigated. The study showed that as the heat treatment temperature increases, the change of carbon fiber resistivity around 1100 °C can be divided into two stages. In the first stage, the carbon content of the fiber increased rapidly, and small molecules such as nitrogen were gradually released to form a turbostratic of carbon crystal structure. The resistivity dropped rapidly from 3.19 × 10− 5 Ω·m to 2.12 × 10− 5 Ω·m. In the second stage, the carbon microcrystalline structure gradually became regular, and the electron movement area gradually became larger. At this time, the resistivity further decreases, from 2.12 × 10− 5 Ω·m to 1.59 × 10− 5 Ω·m. During carbonization, the tensile strength of carbon fiber first increased and then decreased. This is because the irregular and disordered graphite structure is formed first. As the temperature rose, the graphite layer spacing decreased and the grain thickness gradually increases. The modulus also gradually increased.

As goods and services powered by AI continue to proliferate, scholarly opinion seems to consider that current WTO law is insufficient to regulate trade in AI-powered products. The following reasons can help explain this perceived insufficiency of the WTO law: (a) AI-powered products are difficult to categorise within the perceived goods/services dichotomy under WTO law, thus causing uncertainties as to the applicable legal regime; and (b) the WTO law has yet to respond to the need for national governments to strike a balance between trade and controversial trade practices regarding AI-powered products. This paper argues that while current WTO law is far from perfect, it does partly regulate trade in AI-powered products. The following observations substantiate the partial regulation of trade in AI-powered products by the WTO law: (a) AI-powered products cannot escape existing WTO disciplines on trade in goods and trade in services, by virtue of either the involvement of AI or the perceived goods/services dichotomy; and (b) efforts to balance trade/non-trade interests associated with trade in AI-powered products are allowed under the GATT/GATS’ ‘public morals’ and security exceptions.